Flash annealing influence on structural and electrical properties of TiO2/TiO/Ti periodic multilayers
2014
Abstract Multilayered structures with a 40 nm period composed of titanium and two different titanium oxides, TiO and TiO 2 , were accurately produced by DC magnetron sputtering using the reactive gas pulsing process. These multilayers were sputtered onto Al 2 O 3 sapphire to avoid substrate compound diffusion during flash annealing (ranging from 350 °C to 550 °C). Structure and composition of these periodic TiO 2 /TiO/Ti stacks were investigated by X-ray diffraction, X-ray photoemission spectroscopy and transmission electronic microscopy techniques. Two crystalline phases α-Ti and fcc-TiO were identified in the metallic-rich sub-layers whereas the oxygen-rich ones were composed of a mixture…
Structural characterization of TiO2/TiN O (δ-doping) heterostructures on (1 1 0)TiO2 substrates
2003
Abstract TiO2/TiNxOy δ-doping structures were grown on the top of (1 1 0)TiO2 rutile substrates by low pressure metal-organic vapor phase epitaxy (LP-MOVPE) technique at 750 °C. The samples were analyzed by high resolution transmission electron microscopy (HRTEM), electron energy loss spectroscopy (EELS) and X-ray diffraction techniques (rocking curves and φ-scans). The presence of satellites in the (1 1 0)TiO2 rocking curve revealed the epitaxial growth of 10 period δ-doping structures. The thickness of the TiO2 layers, 84 nm, was deduced from the satellites period. HRTEM observations showed around 1.5 nm thick δ-doping layers, where the presence of nitrogen was detected by EELS. The analy…
The interdependence of structural and electrical properties in TiO2/TiO/Ti periodic multilayers
2013
International audience; Multilayered structures with 14-50 nm periods composed of titanium and two different titanium oxides, TiO and TiO2, were accurately produced by DC magnetron sputtering using the reactive gas pulsing process. The structure and composition of these periodic TiO2/TiO/Ti stacks were investigated by X-ray diffraction and transmission electronic microscopy techniques. Two crystalline phases, hexagonal close packed Ti and face centred cubic TiO, were identified in the metallic-rich sub-layers, whereas the oxygen-rich ones comprised a mixture of amorphous TiO2 and rutile phase. DC electrical resistivity rho measured for temperatures ranging from 300 to 500 K exhibited a meta…
Structure and properties of GaNxOy films grown by nitridation of GaAs (100) substrates
2004
GaAs (100) substrates have been heat-treated in a metal-organic chemical vapor deposition reactor under flows of NH 3 and an oxygen organo-metallic precursor at temperatures between 650°C and 750°C. Yellowish films formed at the surface of all the samples. Gallium, nitrogen and oxygen were detected by EDX analysis of the films. The oxygen content was estimated in the range of at 5-10 at% depending on the heat-treatment temperature. X-ray diffraction and HRTEM results indicate that the structure of the films corresponds to the hexagonal wurtzite phase of GaN with an expanded unit cell. Raman spectra show hands corresponding to the Raman active GaN modes as well as disorder-activated broad ba…
The influence of the anatase nanoparticles boundaries on the titania activity performance
2014
Metal oxides structures, formed by ordered self-assembling of crystalline nanoparticles aggregates, are attracting growing attention in fields such as catalysis or solar cells. The properties of these structures are influenced not only by their morphology and nanoparticles composition but also by the assembled particles boundaries. In order to determine the influence of these boundaries on the structures properties, the present investigation has been devoted to study the characteristics of anatase nanoparticles boundaries in titania aggregates prepared by TiCl4 hydrolysis at low temperature. Proton magic angle spinning nuclear magnetic resonance and high resolution transmission electron mic…
Mesocrystalline Cr and Sb-codoped anatase visible-light-driven photocatalyst
2018
Abstract We report on the synthesis, characterization and visible-light-driven photocatalytic activity of mesocrystalline Cr- and Sb-codoped anatase nanoparticles. Discrete and morphologically well-defined assemblies of anatase nanoparticles sized below 100 nm × 50 nm were prepared by hydrothermal aging of aqueous solutions containing titanium alkoxide, chromium acetylacetonate, antimony acetate and triethanolamine (TEOA) as stabilizer. The as-prepared and TEOA-free doped nanoparticles showed similar crystallographic parameters and spectroscopic features. The incorporation of Cr and Sb dopant cations into the anatase nanoparticles was evaluated by Rietveld refinement of X-ray diffraction pa…
Anatase nanoparticles boundaries resulting from titanium tetrachloride hydrolysis
2017
An important factor that governs solar energy transformation into electrical or chemical energy, when using nanoparticles-based devices, is the spatial location of traps limiting electron transport. Evidences have been presented indicating that the electron diffusion is strongly influenced by nanoparticle boundaries, whose characteristics depend on the particles preparation. In the present work we have studied the role of hydrated excess proton structures in the formation of anatase nanoparticles boundaries in samples prepared by TiCl4 hydrolysis at low temperature and strong acidic conditions. The samples, constituted by anatase nanocrystals but, mainly, by amorphous titania, are studied b…
The effect of the surface disordered layer on the photoreactivity of titania nanoparticles
2017
It is well known that the surface of metal oxide catalysts presents, usually, non-crystalline species containing impurities and low coordinated cations, which are observed in HRTEM images as a disordered layer of amorphous phase. Despite of being these species more accessible and less stable than the crystalline catalysts components, they have been rarely considered when analysing the catalyst activity. In this work, we have studied the effect of a treatment with HCl solution at pH = 0 on the characteristics of the disordered layer in two commercial anatase TiO2 samples, using techniques such as TGA, 1H MAS-NMR and HRTEM, and by determining these sample photocatalytic activity for the 4-nit…
Mesocrystalline anatase nanoparticles synthesized using a simple hydrothermal approach with enhanced light harvesting for gas-phase reaction
2018
Mesocrystalline TiO2 nanoparticles were synthesized using a hydrothermal approach. A simple two-step procedure at low temperature (<140 °C) allowed the nucleation of primary particles sized 2–4 nm and their subsequent assembly as almost spherical aggregates sized ≈20 nm. X-ray powder diffraction (XRD), Raman and X-ray photoelectron spectroscopy (XPS) studies, and HRTEM studies confirmed anatase as the unique TiO2 crystalline phase. The mesocrystalline structure of the anatase aggregates was clearly evidenced by HRTEM and SAED results. The mesocrystalline nanopowders exhibit a mesoporous structure with a surface area and pore volume of 63.5 m2 g−1 and 0.22 cm3 g−1, respectively. Ultraviolet …
Hydrothermal-mediated synthesis of orange Cr, Sb-containing TiO 2 nano-pigments with improved microstructure
2017
Abstract A hydrothermal-mediated via was developed to prepare discrete, non-aggregated Cr,Sb-doped rutile nano-pigments. After annealing the Cr- and Sb-containing TiO2 anatase nanocrystals obtained by hydrothermal aging the nano-pigments Cr,Sb-TiO2 were characterized with the aid of X-ray diffraction (XRD) including lattice parameter and crystallite size determination, Raman spectroscopy, field emission scanning and transmission electron microscopies (FESEM and TEM, respectively) including energy-dispersive X-ray (FESEM/EDX) spectroscopy, high resolution transmission electron microscopy (HRTEM) including selected area electron diffraction (SAED), ultraviolet–visible diffuse reflectance (UV–…